Influence of alloying on the tensile strength and electrical resistivity of silver nanowire: copper composites macroscopic wires
Abstract : Composite powders made up of 1 vol. %Ag nanowires (NW) dispersed in Cu were prepared and consolidated into cylinders by spark plasma sintering. One cylinder was sintered at only 400 °C resulting in a nanocomposite sample with no dissolution of the Ag NW into the Cu matrix. The second cylinder was sintered at 600 °C and the Ag NW are dissolved forming Ag/Cu alloy NW. The cylinders served as starting materials for room temperature wire-drawing, enabling the preparation of wires of decreasing diameters. The microstructure of the cylinders and the wires was investigated by electron microscopy and associated techniques. The tensile strength and electrical resistivity were measured at 293 K and 77 K. The nanocomposite and alloy wires show similar UTS values (1100 MPa at 77 K), but alloying, although spatially limited, provoked a significant increase in electrical resistivity (0.56 µΩ cm at 77 K) compared to the nanocomposite wires (0.49 µΩ cm at 77 K).
https://hal.archives-ouvertes.fr/hal-03108715
Contributeur : Open Archive Toulouse Archive Ouverte (oatao) <>
Soumis le : mercredi 13 janvier 2021 - 12:46:36
Dernière modification le : mardi 16 mars 2021 - 16:01:29
Archivage à long terme le : : mercredi 14 avril 2021 - 18:37:47
Contributeur : Open Archive Toulouse Archive Ouverte (oatao) <>
Soumis le : mercredi 13 janvier 2021 - 12:46:36
Dernière modification le : mardi 16 mars 2021 - 16:01:29
Archivage à long terme le : : mercredi 14 avril 2021 - 18:37:47